2205 Stainless steel plate

Thickness：0.3-260mm
Width：1000, 1219, 1500, 2000, 2500, 3000mm etc.
Length：1000, 1500, 2438, 3000, 5800, 6000, 9000, 12000mm etc
PRODUCTS CAN BE CUSROMIZED
Grade(ASTM UNS)：201 202 301 304 304L 321 316 316L 317L 347H 309S 310S 904L S32205 2507 254SMOS 32760 253MA N08926 etc.
Grade (EN)：1.4301, 1.4307, 1.4541, 1.4401, 1.4404 ,1.4571, 1.4438, 1.4539, 1.4547, 1.4529, 1.4562, 1.4410, 1.4878, 1.4845, 1.4828, 1.4876, 2.4858, 2.4819
Technique：Hot rolled or Hot Rolled
Certification：ISO, SGS, BV
Standard：ASTM JIS AISI GB DIN EN
Surface Finished：BA, 2B,NO.1, NO.4, 4K, HL ,8K

产品详情

SPECICATION

Thickness	0.3-200mm
Length:	2000mm, 2438mm, 3000mm, 5800mm, 6000mm,12000mm， etc
Width:	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Standard:	ASTM，AISI，JIS，GB， DIN，EN
Surface:	BA，2B，NO.1，NO.4，12K，HL，8K
Application:	It is widely used in high-temperature and electric industry, medical devices, construction, chemistry, food industry, agriculture, and ship components.It also applies to food and beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen mesh etc.
Certification:	ISO, SGS，BV
Technique:	Cold Rolled Hot Rolled
Edge:	Mill Edge Slit Edge
Grade （ASTM UNS）	Mill Edge Slit Edge

chemical composition:
carbon（C）:	silicon （Si）：	manganese（Mn）：	phosphorus（P）：	sulfur （S）：	chromium（Cr）：	nickel（Ni）：	nitrogen（N）：	molybdenum（Mo）：
≤0.03	1	≤2.00	≤0.03	≤0.02	22 - 23	4.5 - 6.5	≤0.14-0.20	3.0—3.50

Physical properties:
Density of 2205 duplex steel：	7.98g/cm3
Melting point:	1300-1390 ℃
Heat treatment:	Keep the temperature between 1000-1050℃ for 1-2 hours, fast air cooling or water cooling

Mechanical behavior:
tensile strength:	σb≥795Mpa
Yield Strength:	σb≥550Mpa
Elongation rate:	δ≥15%，hardness≤310（HB）

2205 corrosion resistance and main use environment: Compared with 316L and 317L austenitic stainless steel, 2205 duplex stainless steel 2205 alloy has superior performance in resistance to pitting corrosion and crevice corrosion. It has high corrosion resistance. Compared with austenitic, it has The coefficient of thermal expansion is lower and the thermal conductivity is higher. Compared with austenitic stainless steel, duplex stainless steel 2205 alloy has twice its compressive strength. Compared with 316L and 317L, the designer can reduce its weight. Alloy 2205 is especially suitable for the temperature range of -50°F/+600°F. Under strict restrictions (especially for welded structures), it can also be used at lower temperatures.