254mo Stainless steel plate

Thickness:0.3-260mm
Width:1000, 1219, 1500, 2000, 2500, 3000mm etc.
Length:1000, 1500, 2438, 3000, 5800, 6000, 9000, 12000mm etc
PRODUCTS CAN BE CUSROMIZED
Grade(ASTM UNS):201 202 301 304 304L 321 316 316L 317L 347H 309S 310S 904L S32205 2507 254SMOS 32760 253MA N08926 etc.
Grade (EN):1.4301, 1.4307, 1.4541, 1.4401, 1.4404 ,1.4571, 1.4438, 1.4539, 1.4547, 1.4529, 1.4562, 1.4410, 1.4878, 1.4845, 1.4828, 1.4876, 2.4858, 2.4819
Technique:Hot rolled or Hot Rolled
Certification:ISO, SGS, BV
Standard:ASTM JIS AISI GB DIN EN
Surface Finished:BA, 2B,NO.1, NO.4, 4K, HL ,8K
Contact us
产品详情

SPECICATION


Thickness0.3-200mm
Length:2000mm, 2438mm, 3000mm, 5800mm, 6000mm,12000mm, etc
Width:40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Standard:ASTM,AISI,JIS,GB, DIN,EN
Surface:BA,2B,NO.1,NO.4,12K,HL,8K
Application:It is widely used in high-temperature and electric industry, medical devices, construction, chemistry, food industry, agriculture, and ship components.It also applies to food and beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen mesh etc.
Certification:   ISO, SGS,BV
Technique:Cold Rolled Hot Rolled
Edge:Mill Edge Slit Edge
Grade   (ASTM UNS)Mill Edge Slit Edge


chemical composition:
carbon (C) :manganese (Mn):nickel( Ni):silicon (Si):phosphorus( P) :sulfur ( S) :chromium( Cr):copper (Cu):molybdenum (Mo):
≤0.02≤1.0017.5~18.5≤0.8≤0.03≤0.0119.5~20.50.5~1.06.0~6.5


Physical properties:
density:8.24g/cm3
Melting point:1320-1390 ℃
magnetic:without


Mechanical behavior:
tensile strength:σb≥650Mpa
Yield Strength:σb≥310Mpa
Elongation rate:δ≥40%
hardness:182-223(HB)

National standards: UNS S31254、DIN/EN 1.4547、ASTM A240、ASME SA-240。

Corrosion resistance: It is a kind of high corrosion resistance super austenitic stainless steel, developed for halide and acid environment, and is widely used in harsh working conditions such as high concentration chloride ion medium and sea water. In various industrial occasions in acid media, especially in acids containing halide, 254SMO is far superior to other stainless steels, and in some cases can be comparable to Hastelloy and titanium. Low carbon content and high molybdenum content make it have better resistance to pitting corrosion and crevice corrosion, and excellent resistance to intergranular corrosion. It is a cost-effective stainless steel that is used in the chemical industry, desulfurization and environmental protection at home and abroad. widely used。